Structure and dielectric properties of A-site-deficient perovskite Nd(1 − x)/3M x NbO3 (M = Li, Ag; 0 ≤ x ≤ 0.20) ceramics

Jin, Xia ; Guo, Qing Hong ; Bian, Jian Jiang

Journal of materials science, 2012-08, Vol.47 (16), p.6015-6024 [Periódico revisado por pares]

New York: Springer Nature B.V

Texto completo disponível

Citações Citado por
  • Título:
    Structure and dielectric properties of A-site-deficient perovskite Nd(1 − x)/3M x NbO3 (M = Li, Ag; 0 ≤ x ≤ 0.20) ceramics
  • Autor: Jin, Xia ; Guo, Qing Hong ; Bian, Jian Jiang
  • Assuntos: Ceramics ; Crystal structure ; Dielectric loss ; Dielectric properties ; Doping ; Impedance ; Ion currents ; Lithium ; Low frequencies ; Materials science ; Microwave frequencies ; Network analysers ; Perovskites ; Positive temperature coefficient ; Resonant frequencies ; Silver ; X-ray diffraction
  • É parte de: Journal of materials science, 2012-08, Vol.47 (16), p.6015-6024
  • Descrição: Crystal structure and dielectric properties of the A-site-deficient perovskites Nd(1 − x)/3MxNbO3 (M = Li, Ag; 0 ≤ x ≤ 0.20) ceramics were investigated with X-ray diffractometer (XRD), network analyzer, and impedance analyzer. XRD results showed that no secondary phase was observed for Ag-doped specimens. However, a second phase LiNdNb2O7 appeared for Li-doped ones when x ≥ 0.16. The crystal structure at room temperature transformed from orthorhombic (0 ≤ x < 0.16) into tetragonal symmetry (0.16 ≤ x ≤ 0.20) with the increase of x. Complex impedance analysis and the dielectric properties measured at low frequency showed that the dielectric loss in Nd(1 − x)/3MxNbO3 (M = Li, Ag; 0 ≤ x ≤ 0.20) at low frequency was mainly caused by the lithium or silver ionic conduction, which increased with the increase of temperature. However, the dielectric loss originated from the ionic conductivity was frozen at microwave frequency. The dielectric constant (εr) increased with the addition of Ag, whereas it decreased with the increase of Li addition. The pure and Ag-doped specimens exhibited large positive temperature coefficient of resonant frequency (τf), while the τf value changed from positive into negative with the increase of Li addition. The Q × f value increased from 437 to 1,110 GHz in the case of Li doping and 765 GHz in the case of Ag doping, respectively, when x increased from 0 to 0.12. Further increase in x decreased the Q × f values both for the Li- and Ag-doped specimens. Good combined microwave dielectric properties with εr = 153, Q × f = 1,110 GHz and τf = −45 ppm/°C could be obtained for the Li-doped specimen when x = 0.12.
  • Editor: New York: Springer Nature B.V
  • Idioma: Inglês
Voltar para lista de resultados

  • Realização: ABCD-USP USP   Logos de Redes Sociais: Freepik

Buscando em bases de dados remotas. Favor aguardar.