Influence of upward and horizontal growth direction on microstructure and microhardness of an unsteady-state directionally solidified Al-Cu-Si alloy

Araújo, Raimundo Lucivaldo Marães de ; Kikuchi, Rafael Hideo Lopes ; Barros, André Santos ; Gomes, Laércio Gouvea ; Moutinho, Daniel Joaquim da Conceição ; Gonçalves, Fernando de Almeida ; Moreira, Antonio Luciano Seabra ; Rocha, Otávio Fernandes Lima da

Matéria, 2016-03, Vol.21 (1), p.260-269

Rede Latino-Americana de Materiais

Texto completo disponível

Citações Citado por
  • Título:
    Influence of upward and horizontal growth direction on microstructure and microhardness of an unsteady-state directionally solidified Al-Cu-Si alloy
  • Autor: Araújo, Raimundo Lucivaldo Marães de ; Kikuchi, Rafael Hideo Lopes ; Barros, André Santos ; Gomes, Laércio Gouvea ; Moutinho, Daniel Joaquim da Conceição ; Gonçalves, Fernando de Almeida ; Moreira, Antonio Luciano Seabra ; Rocha, Otávio Fernandes Lima da
  • Assuntos: CONSTRUCTION & BUILDING TECHNOLOGY ; MATERIALS SCIENCE, MULTIDISCIPLINARY ; METALLURGY & METALLURGICAL ENGINEERING
  • É parte de: Matéria, 2016-03, Vol.21 (1), p.260-269
  • Descrição: In order to analyze the effect of the growth direction on dendrite arm spacing (λ1) and microhardness (HV) during horizontal directional solidification (HDS), experiments were carried out with the Al-3wt.%Cu-5.5wt.%Si alloy and the results compared with others from the literature elaborated for upward directional solidification (UDS). For this purpose, a water-cooled directional solidification experimental device was developed, and the alloy investigated was solidified under unsteady-state heat flow conditions. Thermal parameters such as growth rate (VL) and cooling rate (TR) were determined experimentally and correlations among VL, TR, λ1 and HV has been performed. It is observed that experimental power laws characterize λ1 with a function of VL and TRgiven by: λ1=constant(VL)-1.1 and λ1=constant(TR)-0.55. The horizontal solidification direction has not affected the power growth law of λ1 found for the upward solidification. However, higher values of λ1 have been observed when the solidification is developed in the horizontal direction. The interrelation of HV as function of VL, TR and λ1 has been represented by power and Hall-Petch laws. A comparison with the Al-3wt.%Cu alloy from literature was also performed and the results show the Si element affecting significativaly the HV values.
  • Editor: Rede Latino-Americana de Materiais
  • Idioma: Inglês;Português
Voltar para lista de resultados

  • Realização: ABCD-USP USP   Logos de Redes Sociais: Freepik

Buscando em bases de dados remotas. Favor aguardar.